100C Max. 4" Width Electric Hot Rolling Press with Variable Speed (Ar Gas Compatible) - MSK-HRP-01

Effective Cylinder Width

96mm

Rolling Gap

Dial Gauge Accuracy

• A 0.16mm thick electrode coated on copper can be pressed into a minimum thickness of  0.1 mm
• A 0.06mm thick electrode coated on copper can be pressed into a minimum thickness of 0.04 mm
• A 0.33mm thick silver/gold can be pressed into a minimum thickness of 0.03 mm

• 100°C maximum for less than one hour
• 80°C continuously
• Recommended Heating Rate: 1.3°C/minute
• Power of Heating Element: 500W
• Temperature Control:
• Precision temperature controller  with  +/-1°C Accuracy

Rate Voltage

Motor

• High torque 24VDC motor with reducing gear (1:75) 
• 0.8A
• Rated power 40W
• Speed Indicator Display: 0~40
• Actual rolling speed: 0~26 mm/sec (Actual Speed = display value * 0.65)

Power Consumption

600W max.

Surface Hardness of Rollers

HRC60-62

Shipping Dimensions

40" x 25" x 25" 

Shipping Weight

190 lbs

Application Notes

Important announcement (please read this before place the order)

• The MSK-HRP-01 roller is specially designed for battery R&D in terms of its advantages as affordable, compact and precise. Please strictly follow the instructions to operate
• Must use acetone to clean rollers' surface after each use
• Never rolling material with hardness > 50HRC
• If the machine will be idle for a long period of time, please apply anti-rust lubricant on the rollers
• The minimum thickness of the rolled sheet should depend on the physical property of the material. Here are some results from our test:
• Please refer to this instruction on how to calculate rolling pressure from roller gap (reference only)

• This rolling press can be used to make free-standing 2D metal nanosheets by a repeated process of folding and calendering stacked metal sheets (See reference below)
•  Reference Articles: 2D Metals by Repeated Size Reduction

• CE Certified
• MET certificate is available upon request at an extra cost
• One year limited warranty with lifetime support
• Rusting and damage due to improper storage condition or maintenance are not covered by warranty

• Please refer to this instruction on how to calculate rolling pressure from roller gap (reference only)
• Analysis of geometric and electrochemical characteristics of lithium cobalt oxide electrode with different packing densities

• Do not touch the surface of the rolling part of the machine when the rollers are heated up or running.
• Due to the influence of working environments, the temperature on the roller surface may be different from the display on the controller. You may calibrate the temperature by EQ-TC-calibrator-LD, and refer to the instruction here from time to time to ensure heating temperature accuracy
• Never roll materials with hardness > 50HRC
• Multi-step thickness calendering needed: While calendering the sample sheet, make each calendering decrement of 0.02mm comparing with sheet original thickness.
• Never calendering decrement over 0.02mmcomparing with original sheet thickness each calendering.
• Heating the cylinder beyond 100ºC results in roller deformation and causes inaccurate, thicker-than-usual rolling yield.
• In order to prolong the lifespan of the roller bearings, regular lubrication is recommended. 
• Clean roller surface for each rolling  and Use acetone to clean and lubricate  when not in use to avoid corrosion
  
• This rolling machine can be used under Ar gas
• It is not allowed to use any MTI product in any hazardous location, especially prohibit from using in Class I environments (flammable gasses & vapor).