400C Max. Refractory Alloy Die, 1/2" I.D. Dry Pellet Pressing Die - EQ-Die-12DHT

EQ-Die-12DHT is a complete pressing die with 0.5 " I.D. is ready for you to make 11- 12 mm diameter sample pellet. SPECIFICATIONS:

Modle	EQ-Die-12DHT
Height	2 3/8" (60 mm)
Diameter	2 " OD  (50mm)
Weight	1.3 Lbs
The whole set  pressing die includes	The die is made of Cr12MoV refractory alloy with Max. working Temperature 400ºC Max. Load: 6 metric Ton One 0.5"  I.D. core die  made of  hardened steel and highly polished  with hardness HRC 50 Ra 0.08μm highly polished steel One steel sleeve for core dies protection Two pushing rods highly polished and perfectly fitted into the die Two steel support plates One pressing pole for releasing sample from dying only One steel cylinder for pushing out the sample
Steps to make sample pellet	Mixing and grinding chemical powder by agate mortar Calcine mixed the powder in a high temp furnace under suitable temperature Grinding calcined powder again by mortar Put calcined powder into the die Pressing sample by a pressing machine under suitable pressure Take out pellet sample from die Sintering the pellet under suitable temperature Then, a new material sample is formed!
Pressing die installation schematic
Instruction
Cautions	Please must always wear protective goggles during operation !!! Please use alcohol to clean the pressing die every time before use and store it in a dry place with antirust oil after used to avoid rusting on the surface because all pressing dies are made by high-stretched carbon steel for achieving high hardness to meet essential requirements of making ceramic or metal samples. Otherwise, the pressing surface could probably get scratched.
Application Note	You may consider using EQ-BNMR for easy mold release. Please click the picture below to order.