Precursor Powder of NCMOH622 for High Capacity NCM Cathode Powder 200g/bottle - EQ-Lib-Pre-NCM622

0.0/5 rating (0 votes)

Description

Lib-PNCM622 is the precursor powder of NCMOH622  for High Capacity NCM Cathode Powder at your own composition.
There are 200 grams in one bottle
Note:  You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use

Specification                                                       

 Package

  200g/bottle in a vacuumed bag

 Composition

  NCMOH622

 Configuration

 Sphere

 Particle size  distribution

D10:4.33 μm
D50:9.89 μm
D90:18.22 μm

 Specific surface area

4.09 m^2/g

 Tap Density

≥1.64 g/cm^3

 Water Content 

wt%<0.36

   

 PPH value 

~ 8.05

 

Mian Element

   Required Content (mol)

Ratio (Ni:Co:Mn)

 

Li

0

0

 

Ni

40.0528

6.503

 

Co

9.6601

1.569

 

Mn

11.8743

1.928

 

Impurity 

Required(ppm)

Typical(ppm)

 

Ca

<300

18

 

Cu

<50

8

 

Fe

<100

18

 

Mg

<300

19

 

Na

<500

232

 

Zn

<100

102

 

SO4

<5000

3300

  Note

MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery.   If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer.




Application Notes
:

  1. Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
  2. Please keep the powder in a vacuum box to avoid moisture.
  3. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.

Share this product

Please type your full name.
Invalid Input
Invalid Input
Invalid Input
Invalid email address.
Invalid Input
Invalid Input
Invalid Input
Invalid Input

Register for new product information:    

Premier Solutions (PS) Pte Ltd Singapore

Please publish modules in offcanvas position.