Precursor Powder of NCMOH811 for High Capacity NCM Cathode Powder 200g/bottle - EQ-Lib-PNCM811

0.0/5 rating (0 votes)

Description

Lib-PNCM811 is the precursor powder of NCMOH811 for High Capacity NCM Cathode Powder at your own composition.
There are 200 grams in one bottle
Note:  You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use

Specification                                                       

 Package

  200g/bottle in a vacuumed bag

 Composition

  NCMOH811

 Configuration

 Sphere

 Particle size  distribution

D10:5.36 μm
D50:11 μm
D90:18.6 μm

 Magnetic substance

102 ppd

 Tap Density

≥1.74 g/cm^3

 Water Content 

wt%<0.5

   

 PH value 

~ 8.38

 

Mian Element

   Required Content (mol)

Ratio (Ni:Co: Mn)

 

Li

0

0

 

Ni

47.7247

7.994

 

Co

6.3195

1.059

 

Mn

5.6562

0.947

 

Impurity 

Required(ppm)

Typical(ppm)

 

Ca

<300

16

 

Cu

<50

1

 

Fe

<100

15

 

Mg

<300

2

 

Na

<500

229

 

Zn

<100

121

 

SO4

<5000

3000

  Note

MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery.   If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer.




Application Notes
:

  1. Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
  2. Please keep the powder in a vacuum box to avoid moisture.
  3. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.