Precursor Powder of (Ni0.8Co0.15Al0.05(OH)2 for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA

0.0/5 rating (0 votes)

Description

EQ-Lib-Pre-NCA is the precursor of NCA  (Ni0.8Co0.15Al0.05 (OH)2) for DIY Li--NCA cathode powder for high capacity Li-Ion cathode at your own composition.
Note:  You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use

Specification                                                       

 Package

  200g/bottle in a vacuumed bag

 Composition

  Ni0.8Co0.15Al0.05(OH)2

 Configuration

 Sphere

 Particle size  distribution

D10:5±0.5μm
D50:13-18μm
D90:30±0.5μm

 Specific surface area

~1.5m2/g

 Tap Density

≥1.8g/cm3

 Water Content

<500ppm

   

 PPH value 

≤11.2

 

Mian Element

   Required  Content

Real Content(%)

 

Li

0

0

 

Ni

80±0.5

80.07

 

Co

15±0.5

15.10

 

Al

5±0.5

4.77

 

Impurity 

Required(ppm)

Typical(ppm)

 

Ca

<300

49.58

 

Cu

<50

ND

 

Fe

<100

96.34

 

Cr

<50

27.51

 

Mg

<300

44.56

 

Na

<500

119.85

 

S

<2000

391.5

 

Zn

<100

4.19

 

Mn

<100

29.98

 

Si

<300

75.23

 

Zr

<5000

390.0

 

Y

<250

            170.12          

  Note

  MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery.   If you need a larger quantity or have the question for IP, we will forward your inquiry to the producer.




Application Notes
:

  1. Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
  2. Please keep the powder in a vacuum box to avoid moisture.
  3. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.